Creep and fatigue crack growth at elevated temperatures

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F02%3A00322317" target="_blank" >RIV/68081723:_____/02:00322317 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Creep and fatigue crack growth at elevated temperatures
Original language description
Engineering investigations of creep and fatigue, frequently involving fracture problems, require practical answers from modeling based on fundamental principles. It has been realized that a model suitable at atomic level may not be appropriate to solve the subsequent difficulties encountered at the macro level. However, the use of meso-fracture mechanics (FM) modeling methods, where definite assumptions and generalizations can be made, could provide an answer in macro-engineering situations. In this paper two crack growth models are described: the first, linking the micro to macro process in creep, while the second model of fatigue crack growth enables use of meso-fracture dynamics in cyclic crack growth at a range of frequencies and temperatures.
Czech name
Šíření únavových trhlin za zvýšených teplot
Czech description
V následujícím příspěvku je řešena problematika šíření únavových trhlin za zvýšených teplot. V příspěvku jsou popsány 2 modely, jeden spojuje makro a mikro procesy za předpokladu creepu, druhý předpokládá růst únavových trhlin.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—

Publication year
2002
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)