Dependence of fracture surface fractal dimension on crack propagation micromechanism.
Result description
Results on fracture surfaces characterisation of the NiCr steel treated by two heat treatment procedures are shown in present investigation. In order to investigate the susceptibility of the investigated steel to intergranular embrittlement, a melt withincreased content of impurity elements has been fabricated and heat treated by embrittling ageing. Fractal analysis has been applied in order to follow the controlling mechanisms of failure in region of stable crack extension and in region of fracture instability. Fractal dimension of fracture surface has been found as dependent of distance from the crack tip, and changes the value based on controlling mechanism of crack propagation. The results obtained in crack propagation direction and in full specimen thickness enabled fracture surface geometry reconstruction.
Keywords
The result's identifiers
Result code in IS VaVaI
Alternative codes found
RIV/61989100:27360/02:00006823
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
čeština
Original language name
Závislost dimenze fraktálu lomové plochy na mechanismu šíření trhliny.
Original language description
Jsou prezentovány výsledky studia lomových ploch Ni-Cr oceli ve dvou stavech tepelného zpracování. S cílem zjistit citlivost této oceli na interkrystalické zkřehnutí, byla připravena tavba se zvýšeným obsahem nečistot, jejíž vzorky byly následně podrobeny zkřehávajícímu žíhání. S využitím fraktální analýzy byly zkoumány změny kontrolujících mechanismů lomového porušení v oblasti stabilního šíření trhliny a v oblasti vzniku lomové nestability. Dimenze fraktálu lomové plochy není monotónní funkcí vzdálenosti od kořene trhliny, a že se v závislosti na kontrolujícím mechanismu šíření trhliny mění. Výsledky fraktální analýzy ve směru šíření trhliny a v celé šířce lomové fronty se staly podkladem pro rekonstrukci geometrie lomové plochy.
Czech name
Závislost dimenze fraktálu lomové plochy na mechanismu šíření trhliny.
Czech description
—
Classification
Type
Jx - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2002
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Hutnické listy
ISSN
0018-8069
e-ISSN
—
Volume of the periodical
57
Issue of the periodical within the volume
6/8
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
9
Pages from-to
46-54
UT code for WoS article
—
EID of the result in the Scopus database
—
Basic information
Result type
Jx - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP
JG - Metallurgy, metal materials
Year of implementation
2002