Cyclic deformation, crack initiation, and low-cycle fatigue.

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F03%3A07033135" target="_blank" >RIV/68081723:_____/03:07033135 - isvavai.cz</a>
Alternative codes found
RIV/68081723:_____/03:00047140
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Cyclic deformation, crack initiation, and low-cycle fatigue.
Original language description
The study of fatigue of materials and structures started in the nineteenth century because of the appearance of service fractures during cyclic loading of components in some branches of developing industries. With the aim of clarifying the sources of thefatigue damage and to find the governing laws, event at this early period material specimens of suitable geometry were produced, and variable mechanical stress or strain was applied to these specimens in various types of testing machines. Two basic approaches were adopted in the study of materials fatigue: (i) the phenomenological description of cyclic deformation and of the fatigue life and fracture, and (ii) the study of the mechanisms of cyclic straining and of fatigue damage.
Czech name
—
Czech description
—

Project
<a href="/en/project/GA106%2F02%2F0584" target="_blank" >GA106/02/0584: Fatigue life and residual fatigue life assessment based on the kinetics of short crack growth</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2003
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)