Evolution of Secondary Phases in Cr-V and Cr-Mo-V Low alloy steels

Original language description

The evolution of secondary phases in Cr-V and Cr-Mo-V low alloy steels was studied. The steels with two levels of chromium (0.9 and 2.5 wt%)were aged in the range of 100 to 5000 hours at 773,853,953 a 993K. In the investigation,a limited transmission electron microscopy experimental program was combined with credible termodynamic predictions (Thermo-Calc).

Czech name

Vývoj sekundárních fází v nízkolegovaných Cr-V a Cr-Mo-V ocelích

Czech description

Byl studován vývoj sekundárních fází v nízkolegovaných Cr-V a Cr-Mo-V ocelích.Oceli s dvěma úrovněmi Cr byly žíhány po doby 100 až 5000 hodin na teplotách 773, 853, 953 a 993K. Dále byla využita transmisní elekronová mikroskopie a termodynamická predikcefázových rovnováh.

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

BJ - Thermodynamics

OECD FORD branch

—

Project

Result was created during the realization of more than one project. More information in the Projects tab.

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2005

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Canadian Metallurgical Quarterly

ISSN

0008-4433

e-ISSN

—

Volume of the periodical

44

Issue of the periodical within the volume

2

Country of publishing house

CA - CANADA

Number of pages

14

Pages from-to

219-232

UT code for WoS article

—

EID of the result in the Scopus database

—