Notch sensitivity of cast AZ31 magnesium alloy
Original language description
Cast AZ31 alloy was found to be totally insensitive to circumferential notches with stress concentration factor of 2.49. An attempt has been made to explain this behaviour on the basis of fractographic determination of the critical crack size and using notch theory based on fracture mechanics. The S-N curve of cast Mg AZ31 alloy exhibits a pronounced knee in the region of 10 to 5 cycles. The endurance limit based on 10 to 7 cycles is 40 MPa.
Czech name
Vrubová citlivost lité hořčíkové slitiny AZ31
Czech description
Bylo zjištěno, že litá hořčíková slitina AZ31 je při únavovém namáhání zcela necitlivá na přítomnost obvodového vrubu s teoretickým součinitelem koncentrace napětí 2,49. Byl učiněn pokus vysvětlit toto chování na základě fraktograficky zjištěné velikostikritické trhliny s použitím vrubové teorie založené na lomově-mechanických představách. S-N křivka slitiny AZ31 vykazuje výrazné koleno v oblasti 10 na 5 cyklů. Smluvní mez únavy na bázi 10 na 7 cyklů je 40 MPa.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/1P05ME804" target="_blank" >1P05ME804: Fatique behaviour of ultra fine-grained copper and magnesium alloy materials</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)