Influence of tensile mean stress on fatigue lifetime of cast superalloy IN713LC
Original language description
The constant lifetime diagram in high-cycle fatigue region was experimentally determined for Ni-base cast superalloy IN713LC at temperature 800°C. Cyclic creep curves exhibit after initial transition a long secondary stage with nearly constant cyclic creep rate. The fatigue crack initiation both on the surface and in material interior at casting defects and following crack propagation is decisive for lifetime in the studied interval of mean stresses and stress amplitudes.
Czech name
Vliv tahového středního napětí na únavovou životnost lité superslitiny IN713LC
Czech description
Experimentálně byl stanoven diagram konstantní únavové životnosti Ni superslitiny IN713LC ve vysokocyklové oblasti při teplotě 800 °C. Křivky cyklického creepu vykazují po počátečním přechodovém stadiu dlouhou sekundární oblast s přibližně konstantní rychlostí cyklického creepu. Únavová životnost ve studovaném intervalu zatížení je determinována iniciací únavových trhlin jak na povrchu, tak na vnitřních licích defektech a následným šířením trhliny.

Project
<a href="/en/project/GA106%2F05%2F2112" target="_blank" >GA106/05/2112: High-cycle fatigue of Ni-base superalloys at high mean stresses</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)