Diffusion study of Fe and Mo in Fe76Mo8B15Cu1 alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F05%3A00030171" target="_blank" >RIV/68081723:_____/05:00030171 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Diffusion study of Fe and Mo in Fe76Mo8B15Cu1 alloy
Original language description
59Fe and 99Mo tracer diffusion in Fe76Mo8B15Cu1 alloy was studied using serial sectioning method in the temperature range 527 ? 649 K. The ribbon-like samples were annealed at 695 K for 1 and 5 hours before the diffusion experiments; the volume fractionof crystalline phase was checked by the Mössbauer spectroscopy. Concentration profiles obtained by sputtering by Ar+ ions in a glow discharge show two distinct branches suggesting that two diffusion paths are operating.
Czech name
Difúzní studie Fe a Mo ve slitině Fe76Mo8B15Cu1
Czech description
Difúze izotopů 59Fe a 99Mo ve slitině Fe76Mo8B15Cu1 byla studována metodou odebírání vstev v teplotním intervalu 527 - 649 K. Páskové vzorky byly ohrívány při teplotě 695 K po 1 hodinu před difúzním experimentem; objemový podíl krystalické fáze byl měřenpomocí Mössbauerovy spektroskopie. Koncentzrační profily získané odprašováním Ar+ ionty doutnavém výboji se sestávají ze dvou částí, které odpovídají dvěma difúzním cestám.

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)