65Zn diffusion on a two-phase eutectic Mg - 33 wt.% al
Original language description
Diffusion of zinc in a two-phase eutectic alloy Mg ? 33 wt.% Al and in its components, Mg ? Al solid solution and in the intermetallic compound Mg17Al12, was studied. The measurement of Zn diffusion coefficient was carried out by radiotracer technique intemperature interval 498 ? 848 K. Zinc is believed to simulate the migration behavior of magnesium. It was observed that the interphase boundaries do not act as short-circuit paths. The study of the stability of the eutectic structure enabled to estimate the mean specific energy of the (Mg)/ Mg17A12 phase interface.
Czech name
Difúze 65Zn ve dvoufázové eutektické slitině Mg - 33 wt.% Al
Czech description
Byla studována difúze zinku ve dvoufázové eutektické slitine Mg ? 33 wt.% Al a jejich komponentách, v tuhém roztoku Mg ? Al a v intermetalické sloucenine Mg17Al12. Merení koeficientu difúze Zn byla provedena pomocí radioizotopové metody v teplotním intervalu 498 - 848 K. O zinku se predpokládá, že simuluje chování horcíku. Bylo pozorováno, že mezifázové hranice se nechovají jako dráhy o vysoké difuzivite. Studium stability eutektické struktury umožnuje odhadnout prumernou specifickou energii fázového rozhraní (Mg)/Mg17A12.

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)