Effect of mean stress on high-cycle fatigue strength of IN 713LC superalloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F06%3A00047067" target="_blank" >RIV/68081723:_____/06:00047067 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Effect of mean stress on high-cycle fatigue strength of IN 713LC superalloy
Original language description
Fatigue strength of Ni base superalloy IN 713LC was experimentally determined at 800 °C in air using load controlled cycling with tensile mean stress. The constant fatigue life diagram has been constructed with particular attention to the influence of small stress amplitudes at high mean stresses. The mechanism of Stage I initiation of fatigue cracks, the role of casting defects and cavities and their effect on the fatigue strength have been discussed.
Czech name
Vliv středního napětí na vysokocyklovou únavovou pevnost superslitiny IN 713LC
Czech description
Experimentálně byla stanovena únavová pevnost niklové superslitiny IN 713LC při 800°C na vzduchu při zatěžování v řízené síle a za působení tahových středních napětí. Byl zkonstruován diagram konstantní únavové životnosti se zvláštním zřetelem na vliv malých amplitud zatěžování při vysokých středních napětích. Byl diskutován mechanizmus iniciace únavových trhlin (Stage I), úloha licích defektů a kavit a jejich vliv na únavovou pevnost.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/GA106%2F05%2F2112" target="_blank" >GA106/05/2112: High-cycle fatigue of Ni-base superalloys at high mean stresses</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)