Failure behaviour of coated structures
Original language description
Results concerning the influence of a through coating crack on the substrate failure are reported. An approximate approach based on calculations of crack mouth opening displacement for thin protective layers is suggested. It is shown that in the case ofa stiffer coating on a more compliant substrate the critical stress for substrate failure decreases.
Czech name
Selhání povlakovaných konstrukcí
Czech description
Výsledky práce se zaměřují na vliv existence povrchových trhlin v povlacích na selhání celé součásti. Byla uvedena přibližná metoda stanovení kritického napětí pro porušení materiálu substrátu založená na velikosti otevření trhliny na povrchu tělesa.
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Journal of Computational and Applied Mechanics
ISSN
1586-2070
e-ISSN
—
Volume of the periodical
7
Issue of the periodical within the volume
2
Country of publishing house
HU - HUNGARY
Number of pages
11
Pages from-to
1-11
UT code for WoS article
—
EID of the result in the Scopus database
—