Influence of stress amplitude superimposed on tensile mean stress on creep/fatigue lifetime of single crystal CM186LC superalloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F07%3A00084557" target="_blank" >RIV/68081723:_____/07:00084557 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Influence of stress amplitude superimposed on tensile mean stress on creep/fatigue lifetime of single crystal CM186LC superalloy
Original language description
The paper presents experimental results of the study of an interaction of high-cycle fatigue with high temperature creep of single crystal CM186LC superalloy at high tensile mean stress. The influence of small stress amplitude superimposed on high mean stress on the lifetime was analyzed for <001> and <111> orientations. The change of the fracture damage mode from creep dominated to fatigue dominated with increasing stress amplitude was documented by fractographic observations.
Czech name
Vliv amplitudy napětí superponované na tahové střední napětí na životnost monokrystalů superslitiny CM186LC
Czech description
V příspěvku jsou presentovány experimentální výsledky studia interakce vysokocyklové únavy s vysokoteplotním creepem monokrystalů superslitiny CM186LC při vysokých tahových středních napětích. Pro orientace <001> and <111> byl analyzován vliv malých amplitud napětí superponovaných na střední napětí. Fraktograficky byla dokumentována změna způsobu porušení z creepového na únavové s rostoucí amplitudou napětí.

Project
<a href="/en/project/GA106%2F05%2F2112" target="_blank" >GA106/05/2112: High-cycle fatigue of Ni-base superalloys at high mean stresses</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)