Mechanism of 88Y diffusion in QE22 alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00307738" target="_blank" >RIV/68081723:_____/08:00307738 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Mechanism of 88Y diffusion in QE22 alloy
Original language description
Diffusion of radioisotope 88Y was studied in magnesium-based alloy QE22 (nominal composition: Mg ? 2 RE ? 2.5 Ag ? 0.6 Zr in wt. %, RE ? rare earth metal) in temperature interval ranging from 648 K to 728 K. Diffusion behavior of the chosen tracer, whichis suitable for diffusion measurements, simulates the typical migration characteristics of mischmetal components in general. Mixture of RE?s used for alloying contains Ce and Nd as principal elements and it is added in QE22 to promote the creep resistance. It was found that yttrium diffuses along dislocations that act as paths of rapid diffusion. Diffusivity of 88Y along dislocations, a2sDd, was estimated.
Czech name
Mechanismus difúze 88Y ve slitině QE22
Czech description
Byla studována difúze 88Y ve slitině na bázi Mg QE22 v teplotním intervalu 648 - 728 K. Difúzní chování vybraného radioizotopu, který je vhodný pro difúzní měření, simuluje obecně typické migrační charakteristiky mischmetal složek. Směs RE prvků požitá pro legování obsahuje Ce a Nd jako hlavní prvky a je přidána do QE22 k podpoření creepové odolnosti. Bylo zjištěno, že ytrium difunduje podél dislokací, které jsou cestami rychlé difúze. Difuzivita 88Y podél dislokací, a2sDd, byla odhadnuta.

Project
<a href="/en/project/GA106%2F05%2F2115" target="_blank" >GA106/05/2115: Diffusion of constituents in Mg-based advanced alloys and composites</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)