Grain Boundary Self-Diffusion in Technical Nickel. 4. The Effect of Sample Fabrication

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00307784" target="_blank" >RIV/68081723:_____/08:00307784 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Grain Boundary Self-Diffusion in Technical Nickel. 4. The Effect of Sample Fabrication

Original language description

Grain boundary self-diffusion in cast commercial purity nickel (99.5%) nickel was studied in the temperature range from 600 °C to 1000 °C. The relative grain orientation was analyzed on the same samples by means of electron backscatter diffraction (EBSD.

Czech name

Autodifúze po hranicích v technickém niklu. 4. Vliv předžíhání vzorku

Czech description

V rozmezí teplot 600?1000 °C byla u litého technického niklu (99.5%) studována autodifúze po hranicích a zároveň relativní orientace zrn prostřednictvím difrakce odražených elektronů (EBSD).

Type

D - Article in proceedings

CEP classification

BM - Solid-state physics and magnetism

OECD FORD branch

—

Project

—

Continuities

Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2008

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection

METAL 2008. Sborník přednášek.

ISBN

978-80-254-1987-8

ISSN

—

e-ISSN

—

Number of pages

8

Pages from-to

—

Publisher name

Tanger

Place of publication

Ostrava

Event location

Hradec nad Moravicí

Event date

May 13, 2008

Type of event by nationality

WRD - Celosvětová akce

UT code for WoS article

—