Characterization of a ternary Al-Pd-Rh alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00313604" target="_blank" >RIV/68081723:_____/08:00313604 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Characterization of a ternary Al-Pd-Rh alloy
Original language description
The characterization of phases in a ternary Al-Pd-Rh compex metallic alloy annealed at 1100 oC for 49 h before (original state) and after differential thermal analysis was performed. In the investigation, light microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, wavelenght dispersive X-ray spestroscopy, and differential thermal analysis were used. The dominant constituent in the original state was characterized as ?-phase.
Czech name
Charakterizace ternární slitiny Al-Pd-Rh
Czech description
Charakterizace fází ternární komplexní slitiny Al-Pd-Rh žíhané předem při 1100 oC po dobu 49 h (původní stav) byla poté provedena pomocí DTA, optické mikroskopie, rastrovací elektronové mikroskopie, energiově disperzní rtg.spektroskopie, vlnově disperznírtg.spektroskopie, diferenciání termické analýzy. Dominantní složka původního stavu byla charakterizována jako ?-fáze.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
<a href="/en/project/GA106%2F07%2F1259" target="_blank" >GA106/07/1259: Quasicrystalline phases in the Al-Pd-TM system</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)