Low cycle fatigue of Eurofer 97

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F08%3A00313808" target="_blank" >RIV/68081723:_____/08:00313808 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Low cycle fatigue of Eurofer 97
Original language description
The low cycle fatigue and creep-fatigue properties of Eurofer 97 were studied. Fatigue tests have been carried out in air or in high vacuum, from room temperature to 550 °C, under total strain control. The softening behaviour as a function of the imposedstrain amplitude and temperature has been analysed in detail. At the highest test temperature, an increase of the subgrain size and carbide coarsening were observed. The microstructure of the specimens was investigated by TEM.
Czech name
Nízkocyklová únava oceli Eurofer 97
Czech description
Vlastnosti oceli Eurofer 97 během zkoušek nízkocyklové únavy a únavy-creepu byly studovány. Únavové zkoušky byly provedeny na vzduchu a ve vysokém vakuu, od pokojové teploty do 550 °C při řízení celkové deformace. Cyklické změkčení materiálu je funkcí vnější celkové amplitudy deformace a teploty. Růst velikosti subzrn a karbidů byl pozorován při nejvyšších teplotách. Mikrostruktura vzorků byla studována pomocí TEM.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)