Prediction of Brittle Fracture of Epoxy-Aluminum Flanging
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00332683" target="_blank" >RIV/68081723:_____/09:00332683 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Prediction of Brittle Fracture of Epoxy-Aluminum Flanging
Original language description
This paper presents a fracture mechanical approach for estimation of critical bending load of different types of aluminum-epoxy flanging and comparison with experimental measurements. For this purpose, several designs of the flanging were investigated. Epoxyaluminum interface is considered as a bi-material notch and prediction of the failure is based on generalized stress intensity factor and generalized fracture toughness.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2009
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů