Fatigue properties and crack growth in Eurofer steel

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F09%3A00332819" target="_blank" >RIV/68081723:_____/09:00332819 - isvavai.cz</a>

Alternative codes found

RIV/00216305:26210/09:PU86377

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

Fatigue properties and crack growth in Eurofer steel

Original language description

Cyclic plastic response of the Eurofer reduced activation ferritic-martensitic steel at room temperature was studied. Strain amplitude was kept constant during cycling. The softening curves in two representation were obtained. The fatigue life curve in NF = f(ea) representation and the cyclic stress-strain curve were determined. The main part of the study was focused on surface relief observation: determination of crack nucleation sites and kinetics of crack growth. The crack growth coefficient kg was measured, allowing the fatigue life predictions based on the kinetics of short crack growth. The fracture surfaces were observed using scanning electron microscopy (SEM). Nucleation sites, striation and other typical fatigue features were detected.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JL - Fatigue and fracture mechanics

OECD FORD branch

—

Project

<a href="/en/project/GA106%2F09%2F1954" target="_blank" >GA106/09/1954: Role of oxide dispersion in fatigue behaviour of ODS type steels</a><br>

Continuities

Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year

2009

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Materiálové inžinierstvo - Materials Engineering

ISSN

1335-0803

e-ISSN

—

Volume of the periodical

16

Issue of the periodical within the volume

3a

Country of publishing house

SK - SLOVAKIA

Number of pages

6

Pages from-to

—

UT code for WoS article

—

EID of the result in the Scopus database

—