Modelling of degradation processes in creep resistant steels through accelerated creep tests after long-term isothermal ageing
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00367195" target="_blank" >RIV/68081723:_____/10:00367195 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Modelling of degradation processes in creep resistant steels through accelerated creep tests after long-term isothermal ageing
Original language description
The accelerated high temperature creep tests were performed on P91, P92 and P23 steels in an effort to obtain a more complete description of the role of microstructural stability of these steels.It has been found that under restricted oxidation due to argon atmosphere microstructural instability is the main detrimental process in the long-term degradation of the creep rupture strength of these steels.
Czech name
—
Czech description
—
Classification
Type
D - Article in proceedings
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/2A-1TP1%2F057" target="_blank" >2A-1TP1/057: The resolution of material and technological innovations for power and chemical facilities of new generation working under high temperatures</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2010
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Article name in the collection
Materials for Advanced Power Engineering 2010
ISBN
978-3-89336-685-9
ISSN
—
e-ISSN
—
Number of pages
10
Pages from-to
1010-1019
Publisher name
Forschungszentrum Jülich GmbH
Place of publication
Liege
Event location
Liege
Event date
Sep 27, 2010
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—