Effect of time-dependent material properties on the crack behavior in the interface of two polymeric materials
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F11%3A00370349" target="_blank" >RIV/68081723:_____/11:00370349 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Effect of time-dependent material properties on the crack behavior in the interface of two polymeric materials
Original language description
Crack penetration through the bimaterial interface of two polymers is investigated numerically. Due to the practical importance of the problem, a crack in a three-layer pipe consisting of a main and two, inner and outer, protective layers is analyzed inthis paper. The prime aim is to formulate the conditions under which the crack stays arrested at the interface between the protective layer and the main pipe or penetrates into the interface and causes failure of the main pipe and consequently of the entire pipe system. The crack tip stress field is described by using a generalized stress intensity factor for cases where the crack touches the interface and the stress singularity exponent differs from 1/2. The results presented here may contribute to a more accurate estimation of the residual lifetime of multilayer pipes.
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Mechanics of Composite Materials
ISSN
0191-5665
e-ISSN
—
Volume of the periodical
47
Issue of the periodical within the volume
2
Country of publishing house
LV - LATVIA
Number of pages
8
Pages from-to
203-210
UT code for WoS article
000291953300006
EID of the result in the Scopus database
—