Comparison of Creep Behaviour and Microstructural Changes in Electrodeposited Ultrafine-grained Nickel and its Particle-reinforced Nanocomposite

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00385821" target="_blank" >RIV/68081723:_____/12:00385821 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Comparison of Creep Behaviour and Microstructural Changes in Electrodeposited Ultrafine-grained Nickel and its Particle-reinforced Nanocomposite
Original language description
On the basic of the creep experimental results the paper reports comparison creep behaviour of electrodeposited ultrafine-grained nickel and its particle-reinforced nanocomposite. The objective of this research was to further improve the knowledge of thecreep behaviour of monolithic nickel and to explore the role of nano-sized SiO2 particles in the potential creep strengthening of electrodeposited Ni nanocomposite. The creep behaviour and microstructure of the pure ultrafine-grained nickel and its nanocomposite reinforced by 2 vol.% nano-sized SiO2 particles were studied at temperatures in the range from 293 to 573 K and at the tensile stresses between 100 to 800 MPa. It was found that the creep resistance of the nanocomposite might be noticeably improved compared to the monolithic nickel. Possible creep mechanisms controlling the creep rate during the creep loading were discussed. The Coble creep as creep rate controlling mechanism was founded improbable.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)