Low Cycle Fatigue and Analysis of the Cyclic Stress-strain Response in Superalloy Inconel 738LC

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00385840" target="_blank" >RIV/68081723:_____/12:00385840 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Low Cycle Fatigue and Analysis of the Cyclic Stress-strain Response in Superalloy Inconel 738LC
Original language description
The paper describes the results of fatigue behavior study on cast polycrystalline nickel based superalloy tested at 23 and 800 °C. Cylindrical specimens of Inconel 738LC were cyclically strained under total strain control to fracture and multiple step tests were performed to study the effect of temperature on the internal and effective cyclic stress components. Fatigue life curves were approximated by the Manson- Coffin and Basquin laws. The resulting curves were shifted to lower fatigue lives with increasing temperature. The evolution of the effective and internal stress components and effective elastic modules were derived from the hysteresis loops which were analyzed according to the statistical theory of hysteresis loop. Cyclic stress-strain response at both temperatures and the changes of internal and effective stress components were discussed in relation to microstructural parameters of the superalloy.
Czech name
—
Czech description
—

Project
<a href="/en/project/GAP204%2F11%2F1453" target="_blank" >GAP204/11/1453: Analysis of cyclic stress components in advanced high-temperature resistant structural materials</a><br>
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)