Creep damage of Al and Al-Sc alloy processed by ECAP

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00385920" target="_blank" >RIV/68081723:_____/12:00385920 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Creep damage of Al and Al-Sc alloy processed by ECAP
Original language description
Experiments were conducted to determine an effect of equal-channel angular pressing (ECAP) on the creep damage and the microstructure of pure aluminium and an Al-Sc alloy. The coarse-grained materials in their as-received states were subjected to ECAP atroom temperature using a die, which had a 90° angle between the channels. Creep tests in tension were performed on the as-pressed samples at 473 K under an applied stress range between 10 to 50 MPa. For comparison purposes, some creep tests were performed also on both investigated materials in their as-received states. Following ECAP and creep testing samples were prepared for examination by scanning electron microscopy (SEM) equipped with an electron back scattering diffraction (EBSD) unit. The observation of the free surfaces of the ECAP samples after creep exposure showed the occurrence of mesoscopic shear bands exceeding considerably an average grain size. The formation of these bands could be influenced by inhomogeneity of microst
Czech name
—
Czech description
—

Project
<a href="/en/project/GPP108%2F10%2FP469" target="_blank" >GPP108/10/P469: Influence of initial crystallographic orientation on creep behaviour of SPD materials</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)