Casting defects and high temperature fatigue life of IN 713LC superalloy

The result's identifiers

  • Result code in IS VaVaI

    <a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00385946" target="_blank" >RIV/68081723:_____/12:00385946 - isvavai.cz</a>

  • Result on the web

    <a href="http://dx.doi.org/10.1016/j.ijfatigue.2011.12.002" target="_blank" >http://dx.doi.org/10.1016/j.ijfatigue.2011.12.002</a>

  • DOI - Digital Object Identifier

    <a href="http://dx.doi.org/10.1016/j.ijfatigue.2011.12.002" target="_blank" >10.1016/j.ijfatigue.2011.12.002</a>

Alternative languages

  • Result language

    angličtina

  • Original language name

    Casting defects and high temperature fatigue life of IN 713LC superalloy

  • Original language description

    High-cycle high temperature fatigue life of a superalloy IN 713 LC in as cast state and after hot isostatic pressing was experimentally determined for symmetrical cycling and cycling with tensile mean stress of 300 MPa. Fatigue tests were conducted at 800°C in laboratory air. It has been found that the hot isostatic pressing improves the fatigue life. Large casting defects are sites of fatigue crack initiation in both states of the alloy. The hot isostatic pressing reduces the size of casting defects, however the broad scatter band of the lifetime data remains. Determination of casting defects size by optical microscopy on metallographic sections and an analysis of the size distribution by extreme value statistics indicates two types of defects: (i) small isolated defects and (ii) defect clusters consisting of complicated interconnected shrinkages in the three-dimensional space. The size distribution of both types of defects follows the extreme value statistics. This enables to estimat

  • Czech name

  • Czech description

Classification

  • Type

    J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

  • CEP classification

    JL - Fatigue and fracture mechanics

  • OECD FORD branch

Result continuities

  • Project

    Result was created during the realization of more than one project. More information in the Projects tab.

  • Continuities

    I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Others

  • Publication year

    2012

  • Confidentiality

    S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Data specific for result type

  • Name of the periodical

    International Journal of Fatigue

  • ISSN

    0142-1123

  • e-ISSN

  • Volume of the periodical

    41

  • Issue of the periodical within the volume

    AUG

  • Country of publishing house

    GB - UNITED KINGDOM

  • Number of pages

    5

  • Pages from-to

    47-51

  • UT code for WoS article

    000303486800007

  • EID of the result in the Scopus database