Phase equilibria in the ternary In?Ni?Sn system at 700 °C
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00391981" target="_blank" >RIV/68081723:_____/13:00391981 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1016/j.intermet.2012.11.021" target="_blank" >http://dx.doi.org/10.1016/j.intermet.2012.11.021</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.intermet.2012.11.021" target="_blank" >10.1016/j.intermet.2012.11.021</a>
Alternative languages
Result language
angličtina
Original language name
Phase equilibria in the ternary In?Ni?Sn system at 700 °C
Original language description
The phase equilibria of the ternary system In?Ni?Sn were investigated experimentally at 700 °C using X-ray diffraction (XRD) and scanning electron microscopy (SEM) including electron micro probe analysis (EMPA) and energy dispersive X-ray spectroscopy (EDX). A corresponding isothermal section was established based on these results. This particular temperature was chosen because it allowed obtaining reliable results within reasonable time. The existence of the ternary phase InNi6Sn5 was confirmed whereasthe ternary compound In2NiSn, reported earlier in literature, was found to be part of a large solid solution field based on binary InNi. The ternary solubility of the binary phases was established, and continuous solid solutions were found between the isostructural phases Ni3Sn LT and InNi3 as well as between Ni3Sn2 HT and InNi2. In addition, this isothermal section could be well reproduced by CALPHAD modelling. The resulting calculated isotherm at 700 °C is presented, too, and compared
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BJ - Thermodynamics
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/OC08053" target="_blank" >OC08053: Phase equilibria in Zn-Sn-X metallic systems for high-temperature lead-free solders</a><br>
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Intermetallics
ISSN
0966-9795
e-ISSN
—
Volume of the periodical
35
Issue of the periodical within the volume
APR
Country of publishing house
GB - UNITED KINGDOM
Number of pages
8
Pages from-to
90-97
UT code for WoS article
000315367300013
EID of the result in the Scopus database
—