Influence of metallic dopants on fracture behaviour of TiB2 based cermets

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00421219" target="_blank" >RIV/68081723:_____/13:00421219 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.12776/amsc.v3i0.112" target="_blank" >http://dx.doi.org/10.12776/amsc.v3i0.112</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.12776/amsc.v3i0.112" target="_blank" >10.12776/amsc.v3i0.112</a>

Result language
angličtina
Original language name
Influence of metallic dopants on fracture behaviour of TiB2 based cermets
Original language description
Titanium diboride (TiB2) - metal composites were prepared by hot-pressing of the TiB2 - Ni and Ta doped TiB2-Ni powders. The obvious limitation of pure TiB2 is the bad sinterability, exaggerated grain growth at temperatures exceeded 2000°C needed for thedensification and brittleness. There is only limited number of approaches how to improve fracture resistance. The method used in this work is based on doping the basic microstructure by above mentioned metals. The positive influence of dopants on the microstructure and fracture behaviour was demonstrated by means of mechanical properties and fractographic analysis. The right selection of dopants led to the refinement of microstructure resulted in the increase of flexural strength up to the level of 700MPa and fracture toughness of 5.0 MPa.m1/2.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JL - Fatigue and fracture mechanics
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2013
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)