Small Punch Tests at Oxide Scales Surface of Structural Steel and Low Silicon Steel

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00434807" target="_blank" >RIV/68081723:_____/14:00434807 - isvavai.cz</a>
Alternative codes found
RIV/00216305:26210/14:PU110545
Result on the web
<a href="http://dx.doi.org/10.1007/s11085-014-9492-5" target="_blank" >http://dx.doi.org/10.1007/s11085-014-9492-5</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s11085-014-9492-5" target="_blank" >10.1007/s11085-014-9492-5</a>

Result language
angličtina
Original language name
Small Punch Tests at Oxide Scales Surface of Structural Steel and Low Silicon Steel
Original language description
This work is focused on the study of the behavior of oxide scale layers grown on two types of steel: plain carbon steel and silicon-alloyed steel. The small punch test method was chosen to study the mechanical properties of oxide scale layers. Several specimens were prepared from both materials and exposed to 1,000 C for different oxidation times to obtain the desired scale layers. When the oxidation process was complete, oxide layers of varying thickness, composed mainly of hematite and magnetite, werecreated. The specimens were used for testing at temperatures between 600 and 900 C.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JK - Corrosion and material surfaces
OECD FORD branch
—

Project
<a href="/en/project/EE2.3.20.0188" target="_blank" >EE2.3.20.0188: Multidisciplinary Team for Research and Development of Heat Processes</a><br>
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)