Creep and microstructural processes in a low-alloy 2.25%Cr1.6%W steel (ASTM Grade 23)
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F15%3A00450056" target="_blank" >RIV/68081723:_____/15:00450056 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1016/j.matchar.2015.08.008" target="_blank" >http://dx.doi.org/10.1016/j.matchar.2015.08.008</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matchar.2015.08.008" target="_blank" >10.1016/j.matchar.2015.08.008</a>
Alternative languages
Result language
angličtina
Original language name
Creep and microstructural processes in a low-alloy 2.25%Cr1.6%W steel (ASTM Grade 23)
Original language description
A low-alloy 2.25%Cr1%Mo steel (ASTM Grade 22) has been greatly improved by the substitution of almost all of the 1%Mo by 1.6%W. The improved material has been standardized as P/T23 steel (Fe?2.25Cr?1.6W?0.25V?0.05Nb?0.07C). The present investigation wasconducted on T23 steel in an effort to obtain a more complete description and understanding of the role of the microstructural evolution and deformation processes in high-temperature creep. Constant load tensile creep tests were carried out in an argon atmosphere in the temperature range 500?650 °C at stresses ranging from 50 to 400 MPa. It was found that the diffusion in the matrix lattice is the creep-rate controlling process. The results of an extensive transmission electron microscopy (TEM) analysisprogramme to investigate microstructure evolution as a function of temperature are described and compared with the thermodynamic calculations using the software package Thermo-Calc. The significant creep-strength drop of T23 steel after
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Materials Characterization
ISSN
1044-5803
e-ISSN
—
Volume of the periodical
109
Issue of the periodical within the volume
NOV
Country of publishing house
US - UNITED STATES
Number of pages
8
Pages from-to
1-8
UT code for WoS article
000365365400001
EID of the result in the Scopus database
—