Film growth and alloy enrichment during anodizing AZ31 magnesium alloy in fluoride/glycerol electrolytes of a range of water contents

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F16%3A00472822" target="_blank" >RIV/68081723:_____/16:00472822 - isvavai.cz</a>

Result on the web

<a href="http://dx.doi.org/10.1016/j.electacta.2016.09.089" target="_blank" >http://dx.doi.org/10.1016/j.electacta.2016.09.089</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.electacta.2016.09.089" target="_blank" >10.1016/j.electacta.2016.09.089</a>

Result language

angličtina

Original language name

Film growth and alloy enrichment during anodizing AZ31 magnesium alloy in fluoride/glycerol electrolytes of a range of water contents

Original language description

The effect of anodizing AZ31 magnesium alloy in a fluoride/glycerol electrolyte containing from 1 to 40 vol.% water on the compositions of the anodic film and the underlying alloy has been investigated. A range of constant current densities and water contents of the electrolyte were employed. Scanning and transmission electron microscopy, with energy-dispersive X-ray spectroscopy, X-ray diffraction and ion beam analyses were used to analyse the anodized alloy. Barrier films, containing fluoride and oxide species, were formed above the matrix, at high current efficiency; a porous film was formed above Al-Mn intermetallic particles. The current density and the water content of the electrolyte affected the O:F atomic ratio and the ionic transport in the films. Significant enrichments of zinc and aluminium were generated in a thin layer of the matrix immediately beneath the film under all conditions of anodizing, with the enrichment of zinc reaching 6.2 x 10(15) at cm(-2) in the enriched alloy layer. The cause of the enrichments and the consequences to film growth are discussed.

Czech name

—

Czech description

—

Type

J_x - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)

CEP classification

JK - Corrosion and material surfaces

OECD FORD branch

—

Project

—

Continuities

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year

2016

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Electrochimica acta

ISSN

0013-4686

e-ISSN

—

Volume of the periodical

219

Issue of the periodical within the volume

NOV

Country of publishing house

GB - UNITED KINGDOM

Number of pages

10

Pages from-to

28-37

UT code for WoS article

000386656700004

EID of the result in the Scopus database

2-s2.0-84988951236