Early damage and fatigue crack initiation at ambient and elevated temperatures in heat resistant austenitic steel

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00493717" target="_blank" >RIV/68081723:_____/18:00493717 - isvavai.cz</a>
Result on the web
<a href="https://doi.org/10.1051/matecconf/201816504008" target="_blank" >https://doi.org/10.1051/matecconf/201816504008</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1051/matecconf/201816504008" target="_blank" >10.1051/matecconf/201816504008</a>

Result language
angličtina
Original language name
Early damage and fatigue crack initiation at ambient and elevated temperatures in heat resistant austenitic steel
Original language description
Fatigue damage at ambient and at elevated temperature has been studied in advanced heat resistant austenitic steel. Cylindrical specimens were subjected to constant strain rate cycling and cycling with dwell in the tensile part of the cycle with different strain amplitudes. Surface relief evolution and initiation of surface and internal cracks were studied using high resolution SEM, FIB cutting, EBSD analysis, foil preparation and STEM imaging.
Czech name
—
Czech description
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2018
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)