Direct SPD-processing to achieve high-ZT skutterudites

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F18%3A00494213" target="_blank" >RIV/68081723:_____/18:00494213 - isvavai.cz</a>

Result on the web

<a href="http://dx.doi.org/10.1016/j.actamat.2018.08.020" target="_blank" >http://dx.doi.org/10.1016/j.actamat.2018.08.020</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.actamat.2018.08.020" target="_blank" >10.1016/j.actamat.2018.08.020</a>

Result language

angličtina

Original language name

Direct SPD-processing to achieve high-ZT skutterudites

Original language description

For mass fabrication of thermoelectric generators a fast, cheap and simple method is required to produce high ZT leg material. It is well known that severe plastic deformation (SPD) enhances the density of defects and dislocations, and also refines the grains to nano-size. These are the essential key parameters for low thermal phonon conductivity. Consequently and as a first example, SPD via high-pressure torsion (HPT) at elevated temperatures in protective gas atmosphere was used to directly consolidate and plastically deform commercial p-type skutterudite powder, DDyFe3CoSb12, (DD stands for didymium) into a dense thermoelectric solid. The HPT-sample exhibited a high figure of merit, ZT > 1.3 at 773 K, much higher than that of the hot-pressed reference sample (HP) from the same powder. The ZT achieved is comparable with ZTs of corresponding high energy ball milled and hot pressed samples (HBM-HP) as well as of ball milled, hot pressed plus HPT processed skutterudites (BM-HP-HPT). The thermoelectric efficiency is even 4% higher. Synchrotron measurements were performed at temperatures from 300 to 825 K in order to evaluate the changes in grain size and dislocation density of the CP-HPT samples before, during and after annealing. SEM and TEM images served to give a better insight into the temperature dependent diversification of the new material. Due to grain refinement and enhanced dislocation density, the CP-HPT material exhibits higher hardness values than the reference sample. The elastic moduli are, within the error bar, the same. With large high-pressure torsion facilities at hand, a new, fast and therefore cheap mass production of thermoelectric leg material directly from powders can be envisaged. This new production technique furthermore warrants high figures of merit but excludes time-consuming ball milling and hot-pressing steps

Czech name

—

Czech description

—

Type

J_SC - Article in a specialist periodical, which is included in the SCOPUS database

CEP classification

—

OECD FORD branch

10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Project

<a href="/en/project/GA17-12844S" target="_blank" >GA17-12844S: Thermal and phase stability of advanced thermoelectric materials</a><br>

Continuities

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year

2018

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Name of the periodical

Acta Materialia

ISSN

1359-6454

e-ISSN

—

Volume of the periodical

159

Issue of the periodical within the volume

OCT

Country of publishing house

GB - UNITED KINGDOM

Number of pages

12

Pages from-to

352-363

UT code for WoS article

000445986300032

EID of the result in the Scopus database

2-s2.0-85052432022