Evolution of Microstructure of Silicon Steel After Pulsating Water Jet Treatment

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F21%3A00532194" target="_blank" >RIV/68081723:_____/21:00532194 - isvavai.cz</a>
Alternative codes found
RIV/68145535:_____/21:00532194
Result on the web
<a href="http://dx.doi.org/10.1007/978-3-030-53491-2_23" target="_blank" >http://dx.doi.org/10.1007/978-3-030-53491-2_23</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/978-3-030-53491-2_23" target="_blank" >10.1007/978-3-030-53491-2_23</a>

Result language
angličtina
Original language name
Evolution of Microstructure of Silicon Steel After Pulsating Water Jet Treatment
Original language description
The present study is focused on the evolution of microstructure of silicon steel (Fe-Si 6 wt%) after treatment by pulsating water jet (PWJ). The various stages of erosion by pulsating water jet have been studied. The initialndamage shows formation of depressions and isolates erosion pits.Repeated passingnof water initialized further pit formation and coalescence of pits to craters. Duringnthis stages small cracks formation was observed. The repeated passing of waterninduced deepening of the craters and material removal. The PWJ caused plasticndeformation and increase of values of hardness of the subsurface region. The cleavage fracture was present on contained eroded surface.
Czech name
—
Czech description
—

Project
<a href="/en/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)