Tribological Behaviour of Carbon Hard Composite Coatings

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081731%3A_____%2F08%3A00315556" target="_blank" >RIV/68081731:_____/08:00315556 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Tribological Behaviour of Carbon Hard Composite Coatings
Original language description
Carbon hard composite coatings were exposed to dynamical load and high temperature pin-on-disc CSM Tribometer. To evaluate the impact resistance of thin hard composite coating in dynamic loading wear applications an impact test was used. The sliding tests in air were carried out in the range from room temperature to 500 °C with controlled relative humidity. Hardness, elastic modulus and fracture toughness of deposited coatings were studied by indentation technique using Fisherscope H100 tester.
Czech name
Tribologické chovaní tvrdých uhlíkových kompozitních vrstev
Czech description
Uhlíkové tvrdé kompozitní povlaky byly vystaveny dynamickému namáhání na impaktním testeru a měření na vysokoteplotním pin-on-disc CSM Tribometru. Testy byly provedeny na vzduchu v teplotním rozsahu od pokojové teploty do 500°C při řízené relativní vlhkosti. Tvrdost, elastický modul a lomová houževnatost deponovaných vrstev byly studovány indentační technikou Fisherscopem H100.

Project
<a href="/en/project/2A-1TP1%2F031" target="_blank" >2A-1TP1/031: *Deposition and properties of modified DLC coatings for industrial application</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)