Raman and AFM piezoresponse study of dense BaTiO3 nanocrystalline ceramics
Original language description
Dense nanocrystalline BaTiO3 (BT) ceramics with grain sizes (GSs) below 100 nm obtained by spark plasma sintering (SPS), were investigated by micro-Raman spectroscopy in order to obtain information about the changes in the local order induced by size effects. The AFM piezoresponse study incontestably proved the ferroelectric switching at local scale in nanocrystalline BaTiO3 ceramics at room temperature
Czech name
Studium husté nanokrystalické keramiky BaTiO3 pomocí Ramanové spektroskopie a metodou AFM piezoodezvy
Czech description
Hustá nanokrystalická keramika BaTiO3 s rozměrem zrn pod 100 nm, připravená technikou "spark plasma sintering" byla studována mikro-ramanovou spektroskopií a metodou AFM piezoodezvy. Přítomnost všech krystalických fáz BaTiO3 i pro keramiky s nejjemnějšístrukturou (rozměr zrn ~ 50 nm) byla prokázána

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2005
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)