Magnetic propertiesof Lu2Fe16X (X = Fe, Ni, Cr, Si) intermetallics under high hydrostatic pressure

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F06%3A00039960" target="_blank" >RIV/68378271:_____/06:00039960 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Magnetic propertiesof Lu2Fe16X (X = Fe, Ni, Cr, Si) intermetallics under high hydrostatic pressure
Original language description
The ferromagnetic state is stabilized by the substitution in all the Lu2Fe16X (X= Ni, Cr, Si) intermetallics. The effect of pressure on TC of the Lu2Fe16Xintermetallics coincides with changes of TC that are induced by hydrogenation in Lu2Fe17Hx. Pressureinduced changes of saturated magnetization of Lu2Fe16X depend on a kind of X-element. Magnetocrystalline anisotropy of Lu2Fe17 is strongly reduced by the substitution of Cr for Fe only
Czech name
Magnetické vlastnosti intermetalických sloučenin Lu2Fe16X (X = Fe, Ni, Cr, Si) za vysokých hydrostatických tlaků
Czech description
Substituce Ni, Cr a Si stabilizují feromagnetický stav ve všech intermetalických sloučeninách typu Lu2Fe16X (X= Ni, Cr, Si). Vliv tlaku na TC v těchto sloučeninách je v souhlase s změnami TC vyvolanými hydrogenací sloučeniny Lu2Fe17. Tlakem vyvolané změny nasycené magnetizace sloučenin Lu2Fe16X závisí na typu prvku X. Magnetokrystalová anizotropie Lu2Fe17 je výrazně snížena pouze substitucí Cr u sloučeniny Lu2Fe16Cr

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2006
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)