Influence of crack orientation on the ductile-brittle behavior in Fe-3 wt.% Si single crystals

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F07%3A00085109" target="_blank" >RIV/68378271:_____/07:00085109 - isvavai.cz</a>
Alternative codes found
RIV/61388998:_____/07:00085109 RIV/68407700:21340/07:04134468
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Influence of crack orientation on the ductile-brittle behavior in Fe-3 wt.% Si single crystals
Original language description
In this paper we present experimental results from fracture tests performed at room temperature on bcc inron-silicon single crystals with edge cracks of two different orientations (001)[110] and (-110)[110]. The cracks were loaded under mode I.
Czech name
Vliv orientace trhliny na tvárně-křehké chování v monokrystalech Fe-3 hm.% Si
Czech description
V tomto článku jsou prezentovány experimentální výsledky lomových zkoušek provedených při pokojové teplotě na monokrystalech Fe-3 hm.% Si s okrajovými trhlinami dvou různých orientací (001)[110] a (-110)[110]. Trhliny byly zatěžovány v tahovém módu I.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)