Quantitative non-destructive indication of decarburized surface layers on steel products

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F11%3A00372511" target="_blank" >RIV/68378271:_____/11:00372511 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Quantitative non-destructive indication of decarburized surface layers on steel products
Original language description
Decarburization is a common adverse effect at manufacturing and processing of steel semi-products. A series of samples was produced from spring steel 54SiCr6 and annealed at 800oC at air atmosphere for 0, 1, 4, 8 and 20 hours. The decarburized layers that appeared on the surfaces were examined metalographically and magnetically. The magnetic hysteresis tests proved an appreciable sensitivity and experimental simpolicity, allowing nondestructive determination of thickness of the decarburized surface layer. Results of the measurement and shape of the calibration curves was shown to depend on surface treatment of the samples
Czech name
—
Czech description
—

Project
<a href="/en/project/GA101%2F09%2F1323" target="_blank" >GA101/09/1323: Nondestructive measurement of steel surfaces decarburization by magnetic methods</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2011
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Article name in the collection
Proceedings of International Conference on Barkhausen Noise and Micromagnetic Testing - ICBM9
ISBN
978-952-67247-4-4
ISSN
—
e-ISSN
—
Number of pages
9
Pages from-to
23-31
Publisher name
ICBM Conference Organisation
Place of publication
Vaajakoski
Event location
Hejnice
Event date
Jun 27, 2011
Type of event by nationality
EUR - Evropská akce
UT code for WoS article
—

Similar results(10)