Growth of Ce doped (Gd,Y)3Al5O12 single crystals by micro-pulling-down method and their scintillation properties

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F12%3A00556938" target="_blank" >RIV/68378271:_____/12:00556938 - isvavai.cz</a>
Result on the web
<a href="https://doi.org/10.1002/pssc.201200263" target="_blank" >https://doi.org/10.1002/pssc.201200263</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1002/pssc.201200263" target="_blank" >10.1002/pssc.201200263</a>

Result language
angličtina
Original language name
Growth of Ce doped (Gd,Y)3Al5O12 single crystals by micro-pulling-down method and their scintillation properties
Original language description
Ce1%:(GdxY1-x)3Al5O12 (x=0, 0.2, 0.4, 0.6 and 0.8) crystals were grown by the μ-PD method. In the range of x=0~0.4, the grown crystals showed single garnet phase, but x=0.6 and 0.8 crystals showed secondary perovskite phase. In these crystals, Ce3+ 4f-5d emission was observed within 500-530 nm wavelength. Emission peaks shifted to shorter wavelength and the decay times was delayed with increasing Gd concentration. The light yield of Ce:(Gd0.6Y0.4)3Al5O12 sample was around 13,000 photon/MeV. Scintillation decay time was around 111 ns.
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
10302 - Condensed matter physics (including formerly solid state physics, supercond.)

Project
—
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2012
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)