Multicomponent (Lu,Y,Gd)3(Ga,Al)5O12 garnets - a new kind of high light yield scintillating material

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F15%3A00456002" target="_blank" >RIV/68378271:_____/15:00456002 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1166/asem.2015.1698" target="_blank" >http://dx.doi.org/10.1166/asem.2015.1698</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1166/asem.2015.1698" target="_blank" >10.1166/asem.2015.1698</a>

Result language
angličtina
Original language name
Multicomponent (Lu,Y,Gd)3(Ga,Al)5O12 garnets - a new kind of high light yield scintillating material
Original language description
Short overview of scintillating properties of multicomponent (Lu,Y,Gd)3(Ga,Al)5O12 garnets and a comparison with properties of Ce3+- and Pr3+- doped single or mixed rare earth aluminum garnets RE3+Al3+O12 where RE are Y, Lu or their mixture in asked ratio, will be presented. The highest light yield up to 27000 ph/MeV was observed on LuAG:Ce while that observed on LuAG:Pr can reach similar to 20000 ph/MeV at 10 microsec long shaping time. These values are almost only one half of those of well prepared multicomponent Gd3Ga3Al2O12:Ce crystal with light yield similar to 50000 ph/MeV.
Czech name
—
Czech description
—

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BM - Solid-state physics and magnetism
OECD FORD branch
—

Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Publication year
2015
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)