Kinetics of static recrystallization in the coarse-grained Fe-40 at.%Al-Zr-B alloy

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F17%3A00502068" target="_blank" >RIV/68378271:_____/17:00502068 - isvavai.cz</a>
Alternative codes found
RIV/46747885:24210/17:00004123 RIV/61989100:27360/17:10238539
Result on the web
<a href="http://dx.doi.org/10.1016/j.acme.2017.03.004" target="_blank" >http://dx.doi.org/10.1016/j.acme.2017.03.004</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.acme.2017.03.004" target="_blank" >10.1016/j.acme.2017.03.004</a>

Result language
angličtina
Original language name
Kinetics of static recrystallization in the coarse-grained Fe-40 at.%Al-Zr-B alloy
Original language description
The aim of works was to describe mathematically the kinetics of static recrystallization of the alloy type Fe–40 at.%Al–Zr–B (with 24.6 Al–0.01 B–0.18 Zr–0.01 C in wt.%) with the coarse- grained structure. The microstructure of the laboratory castings made of this extremely brittle alloy was homogenized by hot rolling of the material in the protective capsules and by the long-term annealing at 1200 °C.n
Czech name
—
Czech description
—

Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20501 - Materials engineering

Project
<a href="/en/project/GAP107%2F10%2F0438" target="_blank" >GAP107/10/0438: Physical and metallurgical aspects of deformation behaviour of iron aluminides with extremely low plasticity</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Publication year
2017
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)