The optical properties of metal oxide nanorods
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F19%3A00517473" target="_blank" >RIV/68378271:_____/19:00517473 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
The optical properties of metal oxide nanorods
Original language description
The different morphological structures were visualized and analyzed by scanning electron microscopy (SEM). The crystalline configuration and the structural quality were investigated by X-ray diffraction and Raman spectroscopy. The surface properties of ZnO nanorods were examined by X-ray photoelectron spectroscopy. The defect-related photoluminescence observed as a broad band at wavelengths 550650 nm was significantly reduced after plasma hydrogenation whereas the exciton-related peak at 378 nm increased significantly. Thus, using hydrogen plasma instead of high temperature annealing, we have achieved the defect passivation at room temperature. The strong suppression of the F+related defects was observed after plasma hydrogenation using the electron paramagnetic resonance (EPR). This makes evidence for strong influence of the surface defects on the photoluminescence properties of the ZnO nanorod.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
—
OECD FORD branch
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2019
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů