ZnMg0.8Ca/Sr0.2 ternary alloys - the influence of the third element on material properties
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F19%3A00538604" target="_blank" >RIV/68378271:_____/19:00538604 - isvavai.cz</a>
Result on the web
<a href="http://dx.doi.org/10.1016/j.prostr.2020.01.054" target="_blank" >http://dx.doi.org/10.1016/j.prostr.2020.01.054</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.prostr.2020.01.054" target="_blank" >10.1016/j.prostr.2020.01.054</a>
Alternative languages
Result language
angličtina
Original language name
ZnMg0.8Ca/Sr0.2 ternary alloys - the influence of the third element on material properties
Original language description
Zinc-based materials alloyed with the elements of the 2nd group of the periodic table have been studied as potential materials for the fabrication of various biodegradable implants. In this study, we prepared two ternary alloys: ZnMg0.8Ca0.2 (wt.%) and ZnMg0.8Sr0.2. The microstructure of both ternary alloys was similar, the main difference was in the size and morphology of the Ca/SrZn13 phase. The SrZn13 phase formed fine particles with a submicron size and had more significant hardening effect in the as-cast state compared to the CaZn13 phase. The annealing led to a transformation of the eutectic structure into the “massive” Mg2Zn11 phase which caused a significant increase of both hardness and compressive yield stress. In the annealed states, comparable hardness was observed for both alloys and higher compressive yield strength for the Ca-containing alloy.
Czech name
—
Czech description
—
Classification
Type
D - Article in proceedings
CEP classification
—
OECD FORD branch
20501 - Materials engineering
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2019
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Article name in the collection
Procedia Structural Integrity
ISBN
—
ISSN
2452-3216
e-ISSN
—
Number of pages
6
Pages from-to
3-8
Publisher name
Elsevier
Place of publication
Brno
Event location
Brno
Event date
Jun 26, 2019
Type of event by nationality
WRD - Celosvětová akce
UT code for WoS article
—