Phase diagram of BaI2-LuI3 system and growth of BaI2/LuI3 eutectic scintillator
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F20%3A00539424" target="_blank" >RIV/68378271:_____/20:00539424 - isvavai.cz</a>
Result on the web
<a href="https://doi.org/10.1016/j.jcrysgro.2020.125573" target="_blank" >https://doi.org/10.1016/j.jcrysgro.2020.125573</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jcrysgro.2020.125573" target="_blank" >10.1016/j.jcrysgro.2020.125573</a>
Alternative languages
Result language
angličtina
Original language name
Phase diagram of BaI2-LuI3 system and growth of BaI2/LuI3 eutectic scintillator
Original language description
The phase diagram of the BaI2-LuI3 system was created using powder X-ray diffraction (XRD) and differential scanning calorimetry (DSC) analyses. Eutectic scintillating crystal of eutectic composition was grown by the vertical Bridgman method. The results of XRD patterns and DSC curves showed that the phase diagram of the BaI2-LuI3 system had a eutectic point around 77.5 mol% BaI2/22.5 mol% LuI3. No new compound was generated from BaI2 and LuI3 mixture. The 77.5 mol% BaI2/22.5 mol% LuI3 eutectic crystal was composed of BaI2 as rod phase and LuI3 as matrix phase. In addition, the Ce-doped 77.5 mol% BaI2/22.5 mol% LuI3 specimen showed emission peaks originating from 5d–4f transition of Ce3+ ion in the X-ray radioluminescence spectrum and the decay time under γ-ray irradiation was approximately 38 ns.
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
20501 - Materials engineering
Result continuities
Project
—
Continuities
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Others
Publication year
2020
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Journal of Crystal Growth
ISSN
0022-0248
e-ISSN
—
Volume of the periodical
536
Issue of the periodical within the volume
Apr
Country of publishing house
NL - THE KINGDOM OF THE NETHERLANDS
Number of pages
5
Pages from-to
1-5
UT code for WoS article
000520838100015
EID of the result in the Scopus database
2-s2.0-85080984163