Luminescence and scintillation properties of Gd3Sc2(Al3-xGax)O12:Ce (x = 1, 2, 3) garnet crystals
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F21%3A00542681" target="_blank" >RIV/68378271:_____/21:00542681 - isvavai.cz</a>
Result on the web
<a href="https://doi.org/10.1016/j.radphyschem.2021.109559" target="_blank" >https://doi.org/10.1016/j.radphyschem.2021.109559</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.radphyschem.2021.109559" target="_blank" >10.1016/j.radphyschem.2021.109559</a>
Alternative languages
Result language
angličtina
Original language name
Luminescence and scintillation properties of Gd3Sc2(Al3-xGax)O12:Ce (x = 1, 2, 3) garnet crystals
Original language description
The luminescence and scintillation characteristics of Ce3+ - doped Gd3Sc2(Al3-xGax)O12 (x = 1, 2, 3) garnet crystals were investigated. The Ce3+ luminescence was blue-shifted with increasing Ga content due to the decrease of the crystal field strength. A decrease of Ce3+ luminescence intensity and luminescence decay time at high temperature was observed for all samples due to thermal ionization of the Ce3+ 5d1 excited levels. With increasing Ga content the decrease of thermal activation energies, determined from temperature dependence of decay times, was obtained. Both Gd3Sc2Al2GaO12:Ce and Gd3Sc2AlGa2O12:Ce samples exhibited a comparable light yield (LY) value of 24,000 photons/MeV while the latter sample showed faster scintillation decay time of 12ns (11%) + 56 ns (89%) with respect to those of 55 ns (28%) + 105 ns (72%) for the former sample. An acceleration of scintillation decay time with an expense of LY value was also obtained for the Mg2+-codoped sample.n
Czech name
—
Czech description
—
Classification
Type
J<sub>imp</sub> - Article in a specialist periodical, which is included in the Web of Science database
CEP classification
—
OECD FORD branch
10302 - Condensed matter physics (including formerly solid state physics, supercond.)
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2021
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Radiation Physics and Chemistry
ISSN
0969-806X
e-ISSN
1879-0895
Volume of the periodical
187
Issue of the periodical within the volume
Oct
Country of publishing house
GB - UNITED KINGDOM
Number of pages
6
Pages from-to
109559
UT code for WoS article
000663797900001
EID of the result in the Scopus database
2-s2.0-85106374731