High Temperature Oxidation of Thermally Sprayed Coatings
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F03%3A02091640" target="_blank" >RIV/68407700:21220/03:02091640 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
High Temperature Oxidation of Thermally Sprayed Coatings
Original language description
This work described high temperature isothermal oxidation of plasma sprayed coatings. For spraying were applied four materials: steel ČSN 17 350 approximately to AISI 316, ČSN 17 021 approximately to AISI 410, unalloyed nickel and NiCr alloy (Ni 80%, Cr20%). Into the experiment were inserted two smelting products into the experiment to compare results of high temperature isothermal oxidation of thermally sprayed coatings: AISI 316 and unalloyed nickel. Grain size of powders was at range of 100 up to 140 mm. The spraying distance (plasma gun nozzle - substrate surface) was 400 mm. A 160 kW water - stabilized plasma gun WPS PAL160 was used for the spraying. As a substrate we used low carbon steel ČSN 11 373 format 100 x 20 x 5 mm. After separation of plasma coatings the thickness of separated coatings did about 1,5 mm and their surface was from 6 to 9 cm2.
Czech name
Není k dispozici
Czech description
Není k dispozici
Classification
Type
A - Audiovisual production
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
—
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)
Others
Publication year
2003
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
ISBN
80-01-02708-2
Place of publication
Praha
Publisher/client name
—
Version
—
Carrier ID
neuvedeno