Microstructure and properties of HVOF-sprayed chromium alloyed WC-Co and WC-Ni coatings

Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F08%3A02149697" target="_blank" >RIV/68407700:21220/08:02149697 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—

Result language
angličtina
Original language name
Microstructure and properties of HVOF-sprayed chromium alloyed WC-Co and WC-Ni coatings
Original language description
The influence of the type of binder metal and chromium as an additional alloying element on the microstructure, mechanical properties and wear resistance of high velocity (HVOF)-sprayed WC-based hardmetal coatings was studied. The coating characterization included optical microscopy and SEM of metallographically prepared cross-sections, hardness measurements, determination of the Youngś modulus and phase composition by X-ray diffraction. The resistance to erosive wear was found to be improved when cobalt was used as binder metal.
Czech name
Mikrostruktura a vlastnosti HVOF nastříkaných povlaků WC-Co a WC-Ni legovaných chromem
Czech description
Vliv typu kovu pojiva a chromu jako přídavného legujícího prvku na mikrostrukturu, mechanické vlastnosti a otěruvzdornost povlaku vysokorychlostním HVOF nástřikem tvrdými kovy byl studován. Charakteristiky povlaku zahrnovaly optickou metalografii a scanmetalograficky připravených příčných řezů, měření tvrdosti, určení modulu pružnosti a fázové složení rtg difrakcí. Odolnost proti erozívnímu opotřebení se zlepšuje, když se použije kobalt jako pojivo.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—

Publication year
2008
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)