Technological Degradation of Shaft Surface During Machining
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F14%3A00222947" target="_blank" >RIV/68407700:21220/14:00222947 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Technological Degradation of Shaft Surface During Machining
Original language description
The paper deals with identifying the causes of surface failure of a shaft made of material 42CrMoS4. On the basis of microstructural analysis completed by hardness testing, the occurrence of undesirable phases, such as non-metallic inclusions in the structure of the shaft, can be demonstrated. In the presence of various heterogeneous phases in the material structure, plucking of particles can occur during chip machining which leads to surface damage. In the conclusion, the authors recommend checking thestarting material, which can eliminate problems that cause the degradation of the surface of the shaft. The failure of the surface causes the notch effect which initiates further failures of the material.
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JG - Metallurgy, metal materials
OECD FORD branch
—
Result continuities
Project
—
Continuities
V - Vyzkumna aktivita podporovana z jinych verejnych zdroju
Others
Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Perner's Contact
ISSN
1801-674X
e-ISSN
—
Volume of the periodical
IX
Issue of the periodical within the volume
2
Country of publishing house
CZ - CZECH REPUBLIC
Number of pages
11
Pages from-to
15-25
UT code for WoS article
—
EID of the result in the Scopus database
—