The Failure Of Carbon Fiber Reinforced Composite Analyzed by Acoustic Emission

Result code in IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F19%3A00334228" target="_blank" >RIV/68407700:21220/19:00334228 - isvavai.cz</a>

Result on the web

—

DOI - Digital Object Identifier

—

Result language

angličtina

Original language name

The Failure Of Carbon Fiber Reinforced Composite Analyzed by Acoustic Emission

Original language description

This paper focus on evaluation of behavior, damage and failure processes occurring during the loading cycles in the carbon fiber reinforced composite by acoustic emission method. Since acoustic emission is physical phenomenon that detects the released energy in form of waves spreading through the material due to stimulation of material by external or internal stress, it is possible to evaluate complex damage and failure processes. For that purpose, the standard and open hole tensile testing specimens with different number of plies were manufactured. Selected acoustic emission parameters were correlated with data obtained from mechanical test. Linear localization method together with signal analysis using Fast Fourier transform algorithm were used as another tool for detection and evaluation of spreading damage processes inside the composite during the load. Basic damage types inside the composite material were identified by metallographic analysis using light microscopy. More complex damage processes were observed on the fracture surface using stereomicroscopy and scanning electron microscopy.

Czech name

—

Czech description

—

Type

O - Miscellaneous

CEP classification

—

OECD FORD branch

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Project

—

Continuities

S - Specificky vyzkum na vysokych skolach

Publication year

2019

Confidentiality

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů