Synthesis and Structural Properties of Mo-Se-C Sputtered Coatings
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F07%3A00140087" target="_blank" >RIV/68407700:21230/07:00140087 - isvavai.cz</a>
Result on the web
—
DOI - Digital Object Identifier
—
Alternative languages
Result language
angličtina
Original language name
Synthesis and Structural Properties of Mo-Se-C Sputtered Coatings
Original language description
Mo-Se-C coatings were prepared by non-reactive r.f. magnetron sputtering from carbon target with embedded MoSe2 pellets. The carbon content and Se/Mo ratio determined by electron probe microanalysis increased from 29 to 68 at.% and from 1.7 to 2.0, respectively, as a function of the decreasing number of pellets. The coating structure analyzed by X-Ray diffraction, Raman spectroscopy and X-ray photoelectron spectroscopy showed that Mo-Se-C was a mixture of amorphous carbon and Mo-Se phases, since no traces of molybdenum carbides were observed. Linear increase of the hardness from 0.7 (29 at.% C) to 4.1 GPa (68 at.% C) showed a significant improvement compared to values typical for pure MoSe2 coating.
Czech name
—
Czech description
—
Classification
Type
O - Miscellaneous
CEP classification
JI - Composite materials
OECD FORD branch
—
Result continuities
Project
<a href="/en/project/GP106%2F07%2FP014" target="_blank" >GP106/07/P014: Self-lubricating coatings based on transition metal dichalcogenides</a><br>
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů