Plasma Spraying and Dielectric Characterization of Zirconium Silicate
Original language description
The article is concerned with selected dielectric properties of zirconium silicate was plasma sprayed. The deposits were tested to measure permittivity and loss factor in the frequency range from 300 Hz to 1 MHz. Dielectric strength was measured in DC regime. The results reveal that also after heating almost to 1000°C the difference between samples, caused by various plasma setup parameters, will manifest itself.
Czech name
Plazmové nástřiky křemičitanu zirkoničitého a jejich dielektrická charakterizace
Czech description
Článek se zabývá vybranými dielektrickými vlastnostmi zirkonsilikátu ve formě plasmových nástřiků. Nástřiky byly měřeny za účelem stanovení jejich permitivity a ztrátového činitele ve frekvenčním rozsahu 300 Hz až 1 MHz. Byla též měřena elektrická pevnost depositů. Výsledky prokazují že i po tepelném ohřevu na 1000°C zůstávají zachovány rozdíly mezi vzorky, jež byly způsobeny odlišnostmi v nastavení parametrů plazmové deposice.

Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
BL - Plasma physics and discharge through gases
OECD FORD branch
—

Project
<a href="/en/project/1QS200430560" target="_blank" >1QS200430560: Progressive thermally sprayed coatings with enhanced wear resistance</a><br>
Continuities
Z - Vyzkumny zamer (s odkazem do CEZ)

Publication year
2007
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Similar results(10)