Sliding properties of Zr-DLC coatings: The effect of tribolayer formation
The result's identifiers
Result code in IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21230%2F14%3A00221398" target="_blank" >RIV/68407700:21230/14:00221398 - isvavai.cz</a>
Alternative codes found
RIV/68407700:21260/14:00221398
Result on the web
<a href="http://dx.doi.org/10.1016/j.surfcoat.2014.08.003" target="_blank" >http://dx.doi.org/10.1016/j.surfcoat.2014.08.003</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.surfcoat.2014.08.003" target="_blank" >10.1016/j.surfcoat.2014.08.003</a>
Alternative languages
Result language
angličtina
Original language name
Sliding properties of Zr-DLC coatings: The effect of tribolayer formation
Original language description
Amorphous carbon-based coatings (DLC) exhibit excellent mechanical and tribological properties such as high hardness, high elastic modulus, low friction and low wear. Reduced friction is often related to the formation of a low-friction tribolayer, whichis formed during sliding and transferred to the counterpart. Here, we investigate the sliding of hydrogenated and non-hydrogenated DLC coatings alloyed with zirconium; pure DLC films are used as reference. The coatings were deposited by magnetron sputtering in Ar (non-hydrogenated) and Ar/methane atmosphere (hydrogenated) onto steel substrates and silicon wafers. The total thickness of the coatings was around 1.5 ?m including a complex Ti/TiN/TiCN adhesion-improving interlayer with a thickness of 450 nm. All deposited coatings were amorphous, Zr/C ratio was approx. 0.05. The hardness was in the range of 9-13 GPa. Tribological tests were carried out in humid air at room temperature, at 100 °C and in nitrogen environment using pin-on-disk
Czech name
—
Czech description
—
Classification
Type
J<sub>x</sub> - Unclassified - Peer-reviewed scientific article (Jimp, Jsc and Jost)
CEP classification
JI - Composite materials
OECD FORD branch
—
Result continuities
Project
Result was created during the realization of more than one project. More information in the Projects tab.
Continuities
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Others
Publication year
2014
Confidentiality
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Data specific for result type
Name of the periodical
Surface and Coatings Technology
ISSN
0257-8972
e-ISSN
—
Volume of the periodical
258
Issue of the periodical within the volume
November
Country of publishing house
NL - THE KINGDOM OF THE NETHERLANDS
Number of pages
12
Pages from-to
734-745
UT code for WoS article
000346895000090
EID of the result in the Scopus database
—